|In this research, it used cement power and reduction slag, which generates high hydration heat in hydration reation without heat cure below -5℃ degree. Purpose of final research is preventing freezing and thawing by making the compressive strength 5MPa in 3days below zero temperature due to own heat of concrete. and it is the result of physical characteristic and thermal property evaluation of reduction slag. Because reduction sag generates high hydration heat, compressive strength development is excellent. By generating highly Hydration heat by C12A7 and C3A in reduction slag, compressive strength is developed in low temperature. In case of displacing only reduction slag without SO3, it is indicated that quick-setting occurs by shortage of SO3. For preventing quick-setting, gypsum is used essentially. According to this research result, in case of using reduction slag and gypsum as a ternary system, Compressive strength developed 5MPa in 3days below zero temperature. It is identified to prevent early frost damage of concrete below zero temperature.